Investigation of Effects of Fire Retardant Chemical Substances on Mold Resistance in Laminate Parquet

Year 2013, Volume: 9 Issue: 1, 14 - 22, 01.03.2013

Ferhat Özdemir Ahmet Tutuş Selim Şen

Abstract

The aim of this study is to determine the effects of certain fire retardant chemicals on mold resistance of laminate flooring. As a source of fiber for high density fiberboard (HDF) panels were used a mixture of %50 yellow pine and beech fibers. HDF panels were produced in 6,5 mm thickness by adding fire retardant chemical materials into fiber. In proportion to complete dry fiber essence fire retardant chemicals borax (BX), boric acid (BA), ammonium polyphosphate (APP) and alpha-x (AX) in pulverized form were added in the ratios of 3%, 6%, and 9%. Afterwards, surfaces of produced HDF boards were coated with overlay, decor and balance sheets and then laminated floorings boards were produced.

Mold resistance of produced laminate flooring was explored. In the test, Aspergillus niger and Aureobasidium pullulans mold were used. To detect mold resistance, the test was made according to ASTM D4445–10. It was determined that 3%, 6%, and 9% additions of fire retardant (FR) chemicals enhanced mold resistance of laminat flooring. As a result, it was ascertained that type of chemical

Keywords

Mold, borax, laminate flooring

Laminat Parkede Yanmayı Geciktirici Kimyasal Maddelerin Küf Mantarı Direnci Üzerine Etkilerinin Araştırılması

Abstract

Bu çalışmanın amacı laminat parkede kullanılan yanmayı geciktirici bazı kimyasal maddelerin küf mantarı üzerine etkilerini belirlemektir. Yüksek yoğunlukta lif levhalar (HDF) için lif kaynağı olarak %50 kayın ve %50 sarıçam kullanılmıştır. Liflerin arasına yanmayı geciktirici kimyasal maddeler eklenerek 6,5 mm kalınlıkta HDF levhalar üretilmiştir. Boraks, borik asit, amonyum polifosfat ve alfa-x yanmayı geciktirici kimyasalları tam kuru lif miktarına oranla %3, %6 ve %9 oranlarında pulverize şekilde eklenmiştir. Daha sonra elde edilen HDF levhaların üzeri overlay, dekor ve balans kâğıtları ile kaplanmış ve laminat parke levhaları üretilmiştir.

Üretilen laminat parkenin küf mantarı direnci araştırılmıştır. Küf mantarı olarak Aspergillus niger and Aureobasidium pullulans mantarları kullanılmıştır. Küf mantarı direncini belirlemek için testler ASTM D 4445–10 standardına göre yapılmıştır. Laminat parkede yanmayı geciktirici kimyasal maddelerin %3, %6 ve %9 oranlarında eklenmesi küf mantarı direncini artırdığı belirlenmiştir. Sonuç olarak, yanmayı geciktirici kimyasal maddelerin türü ve konsantrasyon oranı üretilen laminat parkede küf mantarı direnci üzerine etkili olmuştur.

Keywords

Küf mantarı, boraks, laminat parke, amonyum polifosfat

References

• ASTM D 4445–10. Standard Test Method for Fungicides for Controlling Sapstain and Mold on Unseasoned Lumber (Laboratory Method),
• Ayrılmış, N., Candan, Z., White, R., 2007. Physical, mechanical, and fire properties of oriented strandboard with fire retardant treated veneers. Holz Roh- Werkst 65, 449–45,
• Berkel, A. 1972. Ağaç Malzeme Teknolojisi Cilt II: Ağaç Malzemenin Korunması ve Emprenye Tekniği, İstanbul Üniversitesi Orman Fakültesi, İ.Ü. Yayın No: 1745, O.F.Yayın No: 183, s. 386,
• Fogel, JL., Lloyd, JD, 2002. Mold performance of some construction products with and without borate. Forest Prod. J. 52(2), 38-43,
• İlhan, R. 1999. Ağaç Malzeme Teknolojisi I, Muğla Üniversitesi, Teknik Eğitim Fakültesi, Muğla, s. 165.
• Laks, PE., Quan, X., Palardy, R. D., 2002. Fungal susceptibility of interior commercial building panels. Forest Prod. J. 52(5), 41-44,
• Lloyd, JD., 1998. Borates and Their Biological Applications. The İnternational Research Group on Wood Preservation 29 th Annual Meeting, IRG/WP/98–30178, Maastricht, Nederlands,
• Terzi, E., Kartal, SN., White, RH., Shinoda, K., Imamura, Y., 2011. Fire performance and decay resistance of solid wood and plywood treated with quaternary ammonia compounds and common fire retardants. J. Wood Prod. 69, 41–51,
• Yamaguchi, H. 2003. Silicic acid: Boric Acid Complexes as Wood Preservatives. Wood Sei Technology 37, 287–297,
• Yalınkılıç, MK., Yusuf, S., Yoshimura, T., Takahashi, M., Tsunoda, K. 1996. Effect of Vapor Phaseformalizationof Boric Acid Treated Wood on Boron Leachability and Biological Resistance. İn; Proceedings of Third Pacific RimBio-Based Composite Symposium, Kyoto, Japan, pp. 544–551.