Abrasion resistance and strength properties of non-fibrous and steel fiber reinforced mortars with different aggregates

Year 2018, , 221 - 229, 20.04.2018

Mustafa Karagöz Orhan Canpolat , Mukhallad M. Al-mashhadani , Yurdakul Aygörmez Mucteba Uysal

https://doi.org/10.29187/jscmt.2018.23

Abstract

In this paper, an experimental investigation was carried out to study the effect of using different aggregates

on the abrasion resistance, flexural and compressive strengths of the manufactured OPC mortars. Waste

foundry sand and calcareous limestone were used as a partial replacement with the standard sand. The

aforementioned procedure was conducted with and without the reinforcement of steel fibers in order to

inspect the significance of fibers on the intended tests. Results revealed the fact that using fiber

reinforcement and waste foundry sand together proved to be in benefit of improving the characteristics of

the resulted matrix. MIX 3 yielded the best results in terms of strength properties and abrasion resistance.

Moreover, the mixes with limestone aggregates presented a better performance when compared to the

control specimen.

Keywords

Mortar, Strength Properties, Fibers, Foundry Sand, Abrasion Resistance

References

• 1. Bhardwaj B, Kumar P. Waste foundry sand in concrete : A review. Constr Build Mater. 2017;156:661-674. doi:10.1016/j.conbuildmat.2017.09.010.
• 2. Dolage DAR, Dias MGS, Ariyawansa CT. Offshore Sand as a Fine Aggregate for Concrete Production. Br J Appl Sci Technol. 2013;3(4):813-825.
• 3. Carlos A, Masumi I, Hiroaki M, Maki M, Takahisa O. The effects of limestone aggregate on concrete properties. Constr Build Mater. 2010;24(12):2363-2368. doi:10.1016/j.conbuildmat.2010.05.008.
• 4. Baran M, Bilir T, Canbay E. Use of steel fiber reinforced mortar for seismic strengthening. Constr Build Mater J. 2011;25:892-899. doi:10.1016/j.conbuildmat.2010.06.096.
• 5. Bentur A. Fiber-reinforced cementitious materials. Material science concrete. Ohio: The American Ceramic Society; 1989.
• 6. Bentur A., Mindeness S. fiber reinforced cementitious composites New York: Elsevier Applied Science; 1990.
• 7. Pierre P, Pleau R, Pigeon M. Mechanical properties of steel microfiber reinforced cement pastes and mortars. J Mater Civil Eng 1999; 11(4):317–24.
• 8. BS EN 196-1(2016), BSI Standards Publication Methods of testing cement Part 1: Determination of strength.
• 9. ASTM. (2010). Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens) 1. Chemical Analysis, (C109/C109M – 11b), 1–9. https://doi.org/10.1520/C0109
• 10. ASTM C348. (1998). Standard Test Method for Flexural Strength of Hydraulic-Cement Mortars ASTM C348. Annual Book of ASTM Standards, 4, 2–7. https://doi.org/10.1520/C0348-14.2
• 11. European Standard, EN 1338. Concrete paving blocks – requirements and test, methods; 2003.