AN INVESTIGATION OF PERFORMANCE PROPERTIES OF CURTAIN FABRICS PRODUCED WITH DIFFERENT TYPES OF POLYESTER YARNS

Year 2017, Volume: 27 Issue: 2, 131 - 138, 30.06.2017

Erhan Kenan Çeven , Ayça Gürarda

Abstract

In recent years, curtain has come to a very important place in home textile industry. Curtain, drapery, upholstery, table cloth, sheets and pillowcases, bath accessories, napkins and chair wraps appears to take place within a wide range of home textiles. The textile fabrics most commonly used for home furnishing can be listed as cotton, rayon, linen, nylon, polyester, and their blends. Different techniques have been used by home textile manufacturers to enhance the decorative aspect of the home furnishing products. The most preferred fabrics in home textiles are polyester based fabrics for high durability and ease of use properties. In this study, curtain polyester fabrics with seven different types of weft yarns were woven as samples for the experiments. 300/192 denier 100 % Polyester tight spot (linen like) warp yarn was chosen for all fabrics. The aim of this study is to investigate the breaking strength, breaking elongation, abrasion resistance and air permeability properties of curtain fabrics woven with different types of polyester yarns.

Keywords

Curtain, polyester, air permeability, abrasion resistance, breaking strength

FARKLI TİPTE POLYESTER İPLİKLERLE ÜRETİLMİŞ PERDELİK KUMAŞLARIN PERFORMANS ÖZELLİKLERİNİN ARAŞTIRILMASI

Abstract

Son yıllarda perde, ev tekstili endüstrisi içerisinde oldukça önemli bir yere gelmiştir. Perde, döşemelik kumaş, masa örtüsü, yatak örtüsü, banyo aksesuarları, peçete ve koltuk şalları gibi geniş bir ürün çeşitliliğinin ev tekstilinde yer aldığı görülmektedir. Ev dekorasyonunda en çok kullanılan kumaşlar, pamuk, rayon, keten, nylon, polyester ile bunların bileşimleridir. Ev tekstili üreticileri tarafından ev tekstili ürünlerinde dekoratif etkiyi artırmak için değişik teknikler kullanılmıştır. Ev tekstili ürünlerinde en fazla tercih edilen kumaşların yüksek dayanım ve kullanım kolaylığı açısından polyester esaslı kumaşlar olduğu görülmektedir. Bu çalışmada deneylerde kullanılmak için, yedi farklı özellikte atkı ipliği kullanılarak yedi farklı perdelik polyester kumaş dokutulmuştur. 300/192 denye % 100 polyester tight spot çözgü ipliği tüm numunelerde kullanılmıştır. Bu çalışmanın amacı farklı yapılarda polyester ipliklerden dokunmuş perdelik kumaşların kopma dayanımı, kopma uzaması, aşınma dayanımı ve hava geçirgenliği özelliklerinin araştırılmasıdır

Keywords

Perde, polyester, hava geçirgenliği, aşınma dayanımı, kopma dayanımı

References

• 1. Azeem A., Jahandad N.,Sharjeal A., Ahsan Z., Abdullah S., Bilal R., 2015, “Modeling and Optimization of Performance Properties of Drapery Fabrics Made by Cotton”, International Journal of Textile Science, 4(3), pp:60-65.
• 2. Çeven E.K., Süle G., Gürarda A., Ersöz A., 2011, “Investigation of the Air Permeability Property of Fabrics Woven with Metallic Yarns” Journal of Uludag University Engineering and Architecture Faculty, 16(2), pp: 65-74.
• 3. ASTM D3691/D3691M-09 “Standard Performance Specification for Woven, Lace and Knit Household Curtain and Drapery Fabrics”
• 4. Shahba F.A., 2008, “Production and Characterization of Novel Perfumed Curtain Fabrics”, RJTA, 12(4), pp. 31-40.
• 5. Home Furnishings- A Review. (2016, January 15). Retrieved from http://www.teonline.com/knowledge-centre/home-furnishing.html
• 6. Aydemir H., Demiryürek O., 2014, “Investigation of Breaking Strength, Air Permeability and Water Repellent Properties of Roller Blind Fabrics”, Journal of Erciyes University Science Instıtute, 30(4), pp: 240-247.
• 7. Tayyar A.E., 2010, “Effects of Fabric Parameters on Bursting Strength of Home Textiles”, Journal of Pamukkale University Engineering Faculty, 16(2), pp:165-172.
• 8. İbrahim S.O.K., 2012. “The Effect of Materials Kind Variation on the Functional Performance of the Woven Curtains”, Journal of American Science,8(4),pp:417-425.
• 9. Altaş S., Kadoğlu H., 2009, “The Influence of Some Spinning Parameters on Strength Properties of Core Filament Dref-3 Yarns”, Tekstil ve Konfeksiyon,19(2), pp:93-96.
• 10. Kumpikaitė E., Ragaišienė A., Barburski M., 2010, “Comparable Analysis of the End-Use Properties of Woven Fabrics with Fancy Yarns. Part I: Abrasion Resistance and Air Permeability”, Fibres & Textiles in Eastern Europe, 18 (3), pp.56-59.
• 11. Fan J.,Hunter L., 2009, “Engineering Apparel Fabrics and Garments”, The Textile Institute, pp.170-171.
• 12. Kothari V. K., Timble N. B., 1991, “Air-Jet Texturing: Effect of Jet Type and Some Process Parameters on Properties of Air-Jet Textured Yarns”, Indian Journal of Fibre & Textile Research, 16, pp. 29-38.