Investigation of Electrical, Antibacterial and Performance Characteristics of Fabrics Knitted From Metal Composite Chenille Yarns

Year 2019, , 115 - 126, 30.08.2019

İlkan Özkan , İlhami İlhan

https://doi.org/10.17482/uumfd.480895

Cited By: 2

Abstract

In this study, performance characteristics of
knitted fabrics which produced using metal composite chenille yarns were
investigated. Cotton yarn was folded and twisted with silver-coated polyamide
yarn for producing core yarns of chenille. Composite chenille yarns were
knitted to single jersey fabric. 100% cotton fabric was also produced as
control sample for comparison. Abrasion resistance, circular bending rigidity,
electrical resistance and antibacterial activity tests were applied to samples.
The obtained results were compared and evaluated. As a conclusion, composite
fabrics showed 6 times better abrasion resistance and lower surface resistivity
than control sample. Despite the use of silver in structure, composite fabric
did not show antibacterial activity.

Keywords

Abrasion resistance, Antibacterial activity, Chenille yarn, Circular bending rigidity, Composite yarn, Surface resistivity

METAL KOMPOZİT ŞÖNİL İPLİKLERDEN ÜRETİLMİŞ ÖRME KUMAŞLARIN ELEKTRİKSEL, ANTİBAKTERİYEL VE PERFORMANS ÖZELLİKLERİNİN ARAŞTIRILMASI

Abstract

Bu çalışmada, metal kompozit şönil iplik üretimi gerçekleştirilmiş ve bu
ipliklerden örme kumaş üretilerek performans özellikleri araştırılmıştır. Şönil
ipliğin kararlı yapısını oluşturan bağ iplikleri, gümüş kaplı poliamid filament
ile pamuk ipliğinin katlanıp bükülmesi yoluyla üretilmiştir. Elde edilen
kompozit iplikler örülerek kumaş haline getirilmiş, karşılaştırma amacıyla %100
pamuk ipliğinden kontrol kumaşı da üretilmiştir. Numunelerin aşınma dayanımı,
dairesel eğilme direnci, elektriksel direnci ve antibakteriyel aktivitesinin
belirlenmesi için gerekli testler yapılmıştır. Kompozit kumaş ile kontrol
kumaşından elde edilen sonuçlar karşılaştırılmış ve değerlendirilmiştir.
Kompozit kumaş örneğinin kontrol kumaş örneğinden 6 kat fazla aşınma dayanımına
sahip olduğu, daha düşük yüzey özdirenci gösterdiği ve yapısında gümüş
kullanılmasına karşın antibakteriyel özellik göstermediği bulgusuna
ulaşılmıştır.

Keywords

Antibakteriyel aktivite, Aşınma dayanımı, Dairesel eğilme direnci, Kompozit iplik Şönil iplik, Yüzey özdirenci

References

• 1. İlhan, İ. (2004). Şönil İpliğin Aşınma Direncini Etkileyen Parametreler, Yüksek Lisans Tezi, Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Anabilim Dalı, Adana.
• 2. Hatomoto, I. ve Diğ. (1991). Composite Sheet For Automotive Use, United States Patent, Patent No: 5.009.946 ( https://www.google.ch/patents/US5009946, Erişim Tarihi:16.06.2017)
• 3. Groop, E. E., Nowicki, A. W., Calle, C. I., Buhler, C. R., ve Mantovani, J. G. (2003). Comparison of surface resistivity and triboelectric charge generation characteristics of materials, Proceedings of the 40th Space Congress, Vol. 6.
• 4. Neelakandan, R. ve Madhusoothanan, M., (2010). Electrical resistivity studies on polyaniline coated polyester fabrics. Journal of Engineered Fibers and Fabrics, 5(3), 25-29. Doi: 10.1177/155892501000500304
• 5. Jiang, S., Newton, E., Yuen, C. M. ve Kan, C. (2007). Application of Chemical Silver Plating on Polyester and Cotton Blended Fabric, Textile Research Journal, 2:77-85. Doi: 10.1177/0040517507078739
• 6. Üreyen, M. E., Çavdar, A., Koparalı, A. S., Doğan, A. (2008). Yeni Geliştirilen Gümüş Katkılı Antimikrobiyal Tekstil Kimyasalı ve Bu Kimyasal İle İşlem Görmüş Kumaşların Antibakteriyel Performansları, Tekstil ve Mühendis Dergisi, 15(69): 26-31.
• 7. Hebeish, A., El-Naggar, M. E., Fouda, M. M. G., Ramadan, M. A., Al-Deyab, S. S. ve El-Rafie, M. H. (2011). Highly Effective Antibacterial Textiles Containing Green Synthesized Silver Nanoparticles, Carbohydrate Polymers, 86: 936– 940. Doi: 10.1016/j.carbpol.2011.05.048
• 8. Özkan, İ., ve Duru Baykal, P. (2017) Antifungal activity of fabrics knitted by metalized Silver/Polyester composite yarn, Conference Series: Materials Science and Engineering, Vol. 254, No. 5, IOP Publishing. Doi: 10.1088/1757-899X/254/5/052005
• 9. Choudhury, A. K. R. (2017) Principles of Textile Finishing, Woodhead Publishing.
• 10. Merck Manuals 1, https://www.merckmanuals.com/home/infections/bacterial-infections-gram-positive-bacteria/staphylococcus-aureus-infections, Erişim Tarihi: Haziran, 2018.
• 11. Larry M., Bush, M.D., https://www.merckmanuals.com/home/infections/bacterial-infections-gram-negative-bacteria/klebsiella-,-enterobacter-,-and-serratia-infections, Erişim Tarihi: Haziran, 2018.
• 12. Height, M., https://www.microbe-investigations.com/testing-methods/aatcc-100/, Erişim Tarihi: Haziran, 2018.
• 13. İlhan İ., Özkan İ. ve Yarar A. Y. (2017) İletken Kompozit Şönil İplik Üretimi Üzerine Deneysel Bir Çalışma, Ulusal Çukurova Tekstil Kongresi Bildiriler Kitabı, 373-379.