Evaluation of Translucency Parameters of Resin Composites Colored with Different Solutions

Yıl 2024, Cilt: 13 Sayı: 2, 296 - 302, 20.05.2024

Dilan Kopuz , Özlem Erçin

https://doi.org/10.54617/adoklinikbilimler.1315465

Öz

Aim: To evaluate the translucency parameters of resin composites colored with different solutions.
Materials and Method: 5 different single-shade resin composites; Clearfil Majesty ES-2 Universal, Omnichroma, Vittra APS Unique, ZenChroma, and Charisma Topaz ONE were used. For each group, 28 samples were prepared (7 mm diameter-2 mm thick). Samples were kept in distilled water at 37 °C for 24 hours to complete polymerization. Then, samples were divided into 4 subgroups: colored in coffee, distilled water, red wine, and tea (n=7). The baseline and 28th day, L, a, and b values were measured with a Konica Minolta CM-3600A spectrophotometer using black-and-white backgrounds. Then, the translucency parameters were calculated with CIEDE2000 formula. Data were analyzed using One-Way ANOVA and Tukey tests (p<0.05).
Results: There was a significant difference between the initial and the values after coloration (p<0.05). However, there was no statistically significant difference in the samples kept in distilled water (p>0.05). Before coloration, Omnichroma showed the highest translucency values, while Clearfil Majesty ES-2 Universal showed the lowest. After 28 days of coloring, ZenChroma showed the highest.
Conclusion: Translucency parameter of resin composites were significantly affected by the contents of the solutions, their coloring properties, and the content differences of the materials.

Anahtar Kelimeler

Single-shade resin composite, Spectrophotometer, Translucency

Farklı Solüsyonlarla Renklendirilen Kompozit Rezinlerin Translusensi Parametrelerinin Değerlendirilmesi

Öz

Amaç: Bu çalışmanın amacı, farklı solüsyonlarla renklendirilen kompozit rezinlerin translusensi parametrelerini değerlendirmektir.
Gereç ve Yöntem: Çalışmada 5 farklı tek renkli kompozit rezin; Clearfil Majesty ES-2 Universal, Omnichroma, Vittra APS Unique, ZenChroma ve Charisma Topaz ONE kullanılmıştır. Her bir kompozit rezinden 28 adet (2 mm kalınlığında-7 mm çapında) disk şeklinde örnekler hazırlanmıştır. Polimerizasyonun tamamlanması için örnekler 24 saat 37 °C distile suda bekletilmiştir. Ardından 4 alt gruba ayrılarak: kahve, distile su, kırmızı şarap ve çay solüsyonlarında renklendirilmiştir (n=7). Örneklerin başlangıç ve 28. gün L, a ve b değerleri, Konica Minolta CM-3600A spektrofotometresi ile siyah ve beyaz arka planlar kullanılarak ölçülmüştür. Ardından, örneklerin translusensi parametreleri (TP) CIEDE2000 formülü ile hesaplanmıştır. Veriler One-Way ANOVA ve Tukey testleri kullanılarak analiz edilmiştir (p<0.05).
Bulgular: Örneklerin başlangıç ve renklendirme sonrası değerleri arasında anlamlı farklılıklar bulunurken (p<0.05), sadece distile suda bekletilen örneklerde istatistiksel anlamlılık görülmemiştir (p>0.05). Başlangıçta Omnichroma en yüksek TP değerlerini gösterirken, en düşük TP değerlerini Clearfil Majesty ES-2 Universal göstermiştir. 28 gün renklendirme sonrasında kahve, distile su, kırmızı şarap ve çay solüsyonlarında ZenChroma incelenen materyaller arasında en yüksek TP değerlerini göstermiştir.
Sonuç: Çalışmada kullanılan kompozit rezin materyallerinin translusensi değerleri; solüsyonların içeriklerinden, boyayıcı özelliklerinden ve kompozit materyallerin içerik farklılığından önemli ölçüde etkilenmiştir.

Anahtar Kelimeler

Spektrofotometre, Tek renkli kompozit rezin, Translusensi

Kaynakça

• Hatayama T, Kano Y, Aida A, Chiba A, Sato K, Seki N, et al. The combined effect of light-illuminating direction and enamel rod orientation on color adjustment at the enamel borders of composite restorations. Clin Oral Investig 2020;24:2305-13.
• Yu B, Lee Y-K. Differences in color, translucency and fluorescence between flowable and universal resin composites. J Dent 2008;36:840-6.
• Johnston WM, Reisbick M. Color and translucency changes during and after curing of esthetic restorative materials. Dent Mater 1997;13:89-97.
• Kim IJ, Lee YK. Changes in color and color parameters of dental resin composites after polymerization. J Biomed Mater Res B Appl Biomater 2007;80:541-6.
• Miyagawa Y, Powers JM, O'brien W. Optical properties of direct restorative materials. J Dent Res 1981;60:890-4.
• Perdigão J, Araujo E, Ramos RQ, Gomes G, Pizzolotto L. Adhesive dentistry: Current concepts and clinical considerations. J Esthet Restor Dent 2021;33:51-68.
• Vichi A, Fraioli A, Davidson CL, Ferrari M. Influence of thickness on color in multi-layering technique. Dent Mater 2007;23:1584-9.
• Yu B, Lee Y-K. Influence of color parameters of resin composites on their translucency. Dent Mater 2008;24:1236-42.
• Kim JH, Lee YK, Powers JM. Influence of a series of organic and chemical substances on the translucency of resin composites. J Biomed Mater Res B Appl Biomater 2006;77:21-7.
• Tsubone M, Nakajima M, Hosaka K, Foxton RM, Tagami J. Color shifting at the border of resin composite restorations in human tooth cavity. Dent Mater 2012;28:811-7.
• Foxton RM. Current perspectives on dental adhesion: (2) Concepts for operatively managing carious lesions extending into dentine using bioactive and adhesive direct restorative materials. Jpn Dent Sci Rev 2020;56:208-15.
• Uchida H, Vaidyanathan J, Viswanadhan T, Vaidyanathan TK. Color stability of dental composites as a function of shade. J Prosthet Dent 1998;79:372-7.
• Mjör IA, Moorhead JE, Dahl JE. Reasons for replacement of restorations in permanent teeth in general dental practice. Int Dent J 2000;50:361-6.
• Pérez MM, Ghinea R, Ugarte-Alván LI, Pulgar R, Paravina RD. Color and translucency in silorane-based resin composite compared to universal and nanofilled composites. J Dent 2010;38:110-6.
• da Costa J, Fox P, Ferracane J. Comparison of various resin composite shades and layering technique with a shade guide. J Esthet Restor Dent 2010;22:114-24.
• Pereira Sanchez N, Powers JM, Paravina RD. Instrumental and visual evaluation of the color adjustment potential of resin composites. J Esthet Restor Dent 2019;31:465-70.
• Karataş Ö, Gül P, Akgül N, Çelik N, Gündoğdu M, Duymuş ZY, et al. Effect of staining and bleaching on the microhardness, surface roughness and color of different composite resins. Dent Med Probl 2021;58:369-76.
• Llena C, Fernández S, Forner L. Color stability of nanohybrid resin-based composites, ormocers and compomers. Clin Oral Investig 2017;21:1071-7.
• Demarco FF, Collares K, Coelho-de-Souza FH, Correa MB, Cenci MS, Moraes RR, et al. Long-term survival and reasons for failure in direct anterior composite restorations: A systematic review. Dent Mater 2015;31:1214-24.
• Paolone G. Direct composite restorations in anterior teeth. Managing symmetry in central incisors. Int J Esthet Dent 2014;9:12-25.
• Paolone G, Scolavino S, Gherlone E, Spagnuolo G. Direct esthetic composite restorations in anterior teeth: Managing symmetry strategies. Symmetry 2021;13:797.
• Malekipour MR, Sharafi A, Kazemi S, Khazaei S, Shirani F. Comparison of color stability of a composite resin in different color media. Dent Res J 2012;9:441-6.
• Setcos JC, Tarim B, Suzuki S. Surface finish produced on resin composites by new polishing systems. Quintessence Int 1999;30:169-73.
• Ardu S, Braut V, Gutemberg D, Krejci I, Dietschi D, Feilzer AJ. A long-term laboratory test on staining susceptibility of esthetic composite resin materials. Quintessence Int 2010;41.
• Samra APB, Pereira SK, Delgado LC, Borges CP. Color stability evaluation of aesthetic restorative materials. Braz Oral Res 2008;22:205-10.
• Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part I: core materials. J Prosthet Dent 2002;88:4-9.
• Azzopardi N, Moharamzadeh K, Wood DJ, Martin N, van Noort R. Effect of resin matrix composition on the translucency of experimental dental composite resins. Dent Mater 2009;25:1564-8.
• Fidan M, Yeşilırmak N, Tunçdemir MT. Kahve ile renklendirmenin kompozit rezinlerde renk stabilitesi ve translusensi parametresi üzerindeki etkisinin değerlendirilmesi. NEU Dent J 2021;3:26-32.
• Mikhail SS, Schricker SR, Azer SS, Brantley WA, Johnston WM. Optical characteristics of contemporary dental composite resin materials. J Dent 2013;41:771-8.
• Nikaido T, Kunzelmann K-H, Chen H, Ogata M, Harada N, Yamaguchi S, et al. Evaluation of thermal cycling and mechanical loading on bond strength of a self-etching primer system to dentin. Dent Mater 2002;18:269-75.
• Koyuturk AE, Kusgoz A, Ulker M, Yesilyurt C. Effects of mechanical and thermal aging on microleakage of different fissure sealants. Dent Mater J 2008;27:795-801.