PRODUCTION OF WASTE JUTE DOPED PLA (POLYLACTIC ACID) FILAMENT FOR FFF: EFFECT OF PULVERIZATION

Yıl 2023, Cilt: 7 Sayı: 1, 124 - 128, 29.04.2023

Ayberk Sözen , Alperen Doğru , Murat Demir , Havva Nur Özdemir , Yasemin Seki

https://doi.org/10.46519/ij3dptdi.1213659

Cited By: 1

Öz

In recent years, there has been an outbreak of research on natural fiber-reinforced materials to reduce non-recycled material effects and produce environmentally friendly products. In parallel with the increasing popularity of additive manufacturing, the development of new natural fiber-reinforced materials in this field has also increased to improve pure material characteristics and reduce raw materials usage. This study presents the manufacturing process of %5 waste jute-reinforced PLA filaments and the characteristics of 3D printed parts. For the production of jute-reinforced filaments, polylactic acid (PLA) granules were pulverized to increase the material surface for better bonding between materials in the composite matrix structure. The effectiveness of pulverizing PLA granules was exposed by comparing it with the production of the same composite matrix with PLA granules. Both matrices were formed into filaments to produce 3D parts in Fused Filament Fabrication technology. Thermo-gravimetric analysis (TGA) and differential scanning calorimetry (DSC) will be presented in filament form. Besides, the mechanical properties of 3D parts will also be presented. Within the scope of the study, it is aimed to reveal the material size effect for producing natural fiber-reinforced filaments for additive manufacturing.

Anahtar Kelimeler

PLA, Jute, Additive Manufacturing, FFF, Pulverization

Kaynakça

• 1. Dip, T. M.; Emu. A. S.; Nafiz, M. N. H.; Kundu, P.; Rakhi, H. R.; Sayam, A.; Akhtarujjman, Md.; Shoaib, M.; Ahmed, M. S.; Ushno, S. T. et al.., “3D printing technology for textiles and fashion.” Textile Progress, Vol. 52, Issue 4, Pages 167-260, 2020
• 2. Royan, N. R., Leong, J. S., Chan, W. N., Tan, J. R., & Shamsuddin, Z. S. B. “Current state and challenges of natural fibre-reinforced polymer composites as feeder in fdm-based 3D printing.” Polymers, Vol. 13, Issue 14, 2289, 2021.
• 3. Deb, D., Jafferson, J.M., “Natural fibers reinforced FDM 3D printing filaments.” Materials Today:Proceedings. Vol. 46, Issue 2, Pages 1308-1318, 2021.
• 4. Kariz, M., Sernek, M., Obucina, M., Kuzman, M.K., “Effect of wood content in FDM filament on properties of 3D printed parts.” Materials Today:Communications. Vol. 14, Pages 135-140, 2018.
• 5. Petchwatta, N., Channuan, W., Naknaen, P., Narupai, B., “3D Printing Filaments Prepared from Modified Poly(Lactic Acid)/ Teak Wood Flour Composites: An Investigation on the Particle Size Effects and Silane Coupling Agent Compatibilisation.” Journal of Physical Science. Vol.30, Issue 2, Pages 169-188, 2019.
• 6. Filgueira, D., Holmen, S., Melboss, J.K., Moldes, D., Echtermeyer, A.T., Chinga-Carrasco, G., “Enzymatic-Assisted Modification of Thermomechanical Pulp Fibers To Improve the Interfacial Adhesion with Poly(lactic acid) for 3D Printing.” ACS Sustainable Chem. Eng., Vol. 5, Issue 10, Pages 9338-9346, 2017.
• 7. Le Duigou, A., Barbe, A., Guillou, E., Castro, M., “3D printing of continuous flax fibre reinforced biocomposites for structural applications.” Materials & Design, Vol. 180, 107884. 2019.
• 8. Gama, N., Magina, S., Ferreira, A., Barros-Timmons, A., “Chemically modified bamboo fiber/ABS composites for high-quality additive manufacturing.” Polymer Journal. Vol. 53, Pages 1459-1467., 2021.
• 9. Long, Y., Zhang, Z., Fu, K., Li, Y., “Efficient plant fibre yarn pre-treatment for 3D printed continuous flax fibre/poly(lactic) acid composites.” Composites Part B:Engineering. Vol. 227, 109389, 2021.
• 10. Lacerda, P.S.S., Gama, N., Freire, C.S.R., Silvestre, A.J.D., Barros-Timmons, A., “Grafting Poly(Methyl Methacrylate) (PMMA) from Cork via Atom Transfer Radical Polymerization (ATRP) towards Higher Quality of Three-Dimensional (3D) Printed PMMA/Cork-g-PMMA” Materials. Vol. 12, Issue 9, 1867, 2020.