Synthesis, Characterization and Optimum Reaction Conditions of Oligo-N-Salicylidenephenylhydrazone via Oxidative Polymerization

Yıl 2018, Cilt: 5 Sayı: 2, 919 - 930, 01.01.2018

FEYZA Kolcu

https://doi.org/10.18596/jotcsa.374150

Cited By: 1

Öz

The oxidative polycondensation reaction conditions and
optimum parameters of N-salicylidenephenylhydrazone (SPH) were determined using
air, H₂O₂ and NaOCl as oxidants at a temperature range
between 50 °C and 95 °C in an aqueous alkaline medium. The molecular structures
of the obtained monomer and oligomer were confirmed by FT-IR, UV-Vis, ¹H-NMR and elemental analyses. The
characterization was fulfilled by TG-DTA, size exclusion chromatography (SEC)
and solubility tests. The conversion of N-salicylidenephenylhydrazone into oligomer
was performed using air, H₂O₂ and NaOCl as oxidants in an
aqueous alkaline medium. According to SEC analysis, the number-average
molecular weight (M_n), weight-average molecular weight (M_w)
and polydispersity index (PDI) values of oligo-N-salicylidenephenylhydrazone
(OSPH) obtained using NaOCl oxidant were found to be 1436 g mol-1, 1631 g mol^-1
and 1.14, respectively. The conversion yield of N-salicylidenephenylhydrazone
into oligo-N-salicylidenephenylhydrazone was 100% at optimum reaction
conditions such as [SPH]₀ = [KOH]₀ = [H₂O₂]₀
=0.06, mol/L and at 90 °C for 10 h. Also, according to TG-DTA analysis,
oligo-N-salicylidenephenylhydrazone was shown to be thermally stable and
resistant to thermo-oxidative decomposition. The weight loss of OSPH was found to be 20, 50 and 92.56% at 275°, 597°
and 1000 °C, respectively.

Anahtar Kelimeler

oligo-N-salicylidenephenylhydrazone, oxidative polycondensation, reaction conditions

Kaynakça

• 1. Katon JE, editor. Organic Semiconducting Polymers. Marcel Dekker: New York, NY, USA, 1968.
• 2. El-Shekeil AG, Al-Yusufy FA, Saknidy S. Synthesis and characterization of some soluble conducting polyazomethine polymers. Polym. Int. 1997;44:78-82.
• 3. Diaz FR, Moreno J, Tagle LH, East GA. Radic, D. Synthesis, characterization and electrical properties of polyimines derived from selenophene. Synthetic Met. 1999;100:187-193.
• 4. Ragimov AV, Mamedov BA, Yasamova SY. New efficient dielectric and antistatic materials based on oligoaminophenols. Polymer 1997;43:343-347.
• 5. Kaliyappan T, Kannan P. Co-ordination polymers. Prog. Polymer Sci. 2000;25:343-370.
• 6. Kaya İ, Demir HÖ, Vilayetoğlu AR. The synthesis and characterization of planar oligophenol with Schiff base substituent. Synthetic Met. 2002;126:183-191.
• 7. Kaya İ, Cihangiroğlu N. Synthesis, characterization and anti-microbial activity of oligo-N-2-aminopyridinylsalicylaldimine and some oligomer-metal complexes. J. Poly. Res. 2004;11:37-42.
• 8. Fakhari AR, Khorrami AR, Naeimi H. Synthesis and analytical application of a novel tetradentate N2O2 Schiff base as a chromogenic reagent for determination of nickel in some natural food samples. Talanta 2005;66:813-817.
• 9. Grigoras M, Catanescu CO. Imine oligomers and polymers. J. Macromol. Sci-Pol R 2004;C44:131-173.
• 10. Ayyagari MS, Marx KA, Tripathy SK, Akara JA, Kaplan DL. Controlled free-radical polymerization of phenol derivatives by enzyme-catalyzed reactions in organic solvents. Macromolecules 1995;28:5192-5197.
• 11. Kaya İ, Gökpınar M, Kamacı M. Reaction Conditions, Photophysical, Electrochemical, Conductivity, and Thermal Properties of Polyazomethines. Macromol. Res. 2017;25:739-748.