Evaluation Of The Effect Of Coloration With Coffee On Color Stability And Translucency Parameter In Composite Resins

Yıl 2021, Cilt: 3 Sayı: 1, 26 - 32, 30.04.2021

Muhammet Fidan , Nurcihan Yeşilırmak Makbule Tuğba Tuncdemır

Öz

Aim: The aim of this in vitro study to evaluate the effect of coffee on color change and translucency parameter (TP) in different composite resins.
Material and Methods: In the study, a total of 45 samples from three different composite resins (Estelite Σ Quick, G-Aenial Anterior; Omnichroma), 15 samples in each composite resin group, were prepared with the help of disc-shaped teflon molds of 8 mm diameter and 2 mm depth. After the samples were kept in distilled water for 24 hours, initial color measurements were made with the aid of a spectrophotometer. After staining with coffee for 12 days, second color measurements were repeated. Color changes (ΔE00) and translucency parameter (TP00) of composite resin samples were determined using the CIEDE 2000 color formula before and after coloration with coffee. The data obtained were statistically analyzed with one-way analysis of variance (One-way ANOVA), factorial ANOVA and t test (p <0.05).
Results: A clinically noticeable color change (ΔE00) was detected in composite resin samples kept in coffee for 12 days, with ΔE00 values ranging from 3.28 to 6.28. It was found that the highest color change was in the Omnichroma composite resin group and the lowest color change was in the Estelite Σ Quick composite resin group (p <0.05). Before and after staining with coffee, the Omnichroma composite resin group showed the highest TP values among the examined materials (p <0.05). After staining with coffee, TP value of Omnichroma composite resin group increased, while TP values of other composite resins decreased. Staining with coffee not affected the TP values of the Estelite Σ Quick composite resin group.
Conclusion: Staining with coffee causes color and translucency change in composite resins and optical properties differ between materials. Knowing the optical properties of the restorative material to be preferred in restorations where aesthetics are at the forefront is necessary for long-lasting restorations.

Anahtar Kelimeler

Composite resin, Color stability, Translucency parameter

Kahve ile Renklendirmenin Kompozit Rezinlerde Renk Stabilitesi ve Translusensi Parametresi Üzerindeki Etkisinin Değerlendirilmesi

Öz

Amaç: Bu in vitro çalışmanın amacı; kahvenin farklı kompozit rezinlerde renk değişimine ve translusensi parametresi (TP) üzerine etkisini değerlendirmektir.
Gereç ve Yöntemler: Çalışmada, üç farklı kompozit rezinden (Estelite Σ Quick, G-Aenial Anterior; Omnichroma) her kompozit rezin grubunda 15 örnek olacak şekilde toplamda 45 örnek 8 mm çapında ve 2 mm derinliğinde disk şeklinde teflon kalıplar yardımı ile hazırlandı. Örnekler, 24 saat distile su içerisinde bekletildikten sonra başlangıç renk ölçümleri bir spektrofotometre yardımı ile yapılmıştır. 12 gün boyunca kahve ile renklendirme sonrası ikinci renk ölçümleri tekrarlanmıştır. Kompozit rezin örneklerin renk değişimleri (ΔE00) ve translüsensi parametresi (TP00) kahve ile renklendirme önce ve sonrasında CIEDE 2000 renk formülü kullanılarak belirlenmiştir. Elde edilen veriler tek yönlü varyans analizi (One-way ANOVA), faktöriyel ANOVA ve t testi ile istatistiksel analize tabii tutulmuştur (p<0.05).
Bulgular: 12 gün kahvede bekletilen kompozit rezin örneklerinde klinik olarak fark edilebilir derecede renk değişimi (ΔE00) tespit edilmiştir ve ΔE00 değerleri 3,28 ile 6,28 arasında değişmektedir. En yüksek renk değişiminin Omnichroma kompozit rezin grubunda, en düşük renk değişiminin ise Estelite Σ Quick kompozit rezin grubunda olduğu bulunmuştur (p<0.05). Kahve ile renklendirme önce ve sonrasında Omnichroma kompozit rezin grubu incelenen materyaller arasında en yüksek TP değerleri göstermiştir (p<0.05). Kahve ile renklendirme sonrası Omnichroma kompozit rezin grubunun TP değeri artarken, diğer kompozit rezinlerde TP değerlerinde azalma olmuştur. Kahve ile renklendirme Estelite Σ Quick kompozit rezin grubunun TP değerlerini etkilememiştir.
Sonuç: Kahve ile renklendirme kompozit rezinlerde renk ve translusensi değişimine neden olmakta ve optik özellikler materyaller arasında farklılıklar göstermektedir. Estetiğin ön planda olduğu restorasyonlarda tercih edilecek restoratif materyalin optik özelliklerinin bilinmesi uzun ömürlü restorasyonlar için gereklidir.

Anahtar Kelimeler

Kompozit rezin, Renk stabilitesi, Translusensi parametresi

Kaynakça

• Salas M, Lucena C, Herrera LJ, Yebra A, Della Bona A, Pérez MM. Translucency thresholds for dental materials. Dent Mater. 2018;34:1168–74.
• ElSayad II. Color and translucency of finished and unfinished esthetic restorative materials after staining and bleaching. Saudi Dent J. 2018;30:219–25.
• Çelik N, Sağsöz O, Gündoğdu M. Farklı içeceklerin posterior kompozitlerin renk değişikliği ve yüzey pürüzlülüğü üzerine etkisinin değerlendirilmesi. J Dent Fac Atatürk Uni. 2017;27:27–33.
• Spina DRF, Grossi JRA, Cunali RS, Baratto Filho F, Cunha LF da, Gonzaga CC, et al. Evaluation of discoloration removal by polishing resin composites submitted to staining in different drink solutions. Int Sch Res Not. 2015;2015:1–5.
• Kazemi Yazdi H, Nasoohi N, Benvidi M. In vitro efficacy of listerine whitening mouthwash for color recovery of two discolored composite resins. Front Dent. 2019;16:186.
• Ruchi Gupta, Arvind Bhatheja, Ashvin G John, Midhun Ramchandran, Afnan Ajaz Raina AB, Behera A, et al. Effect of beverages on color stability of resin composites: An in vitro study. Int J Appl Dent Sci. 2019;5:92–5.
• Müdüroğlu R, Çongara Kivrak T, Nalçaci A. Renk belirlenmesinde kullanılan yöntem ve cihazlar. Cumhur Dent J. 2018;21:61–9.
• Fani G, Vichi A, Davidson CL. Spectrophotometric and visual shade measurements of human teeth using three shade guides. Am J Dent. 2007;20:142-6.
• Chen H, Huang J, Dong X, et al. A systematic review of visual and instrumental measurements for tooth shade matching. Quintessence Int. 2012;43:649-59.
• Yildirim B, Recen D, Tekeli Simsek A. Effect of cement color and tooth-shaded background on the final color of lithium disilicate and zirconia-reinforced lithium silicate ceramics: An in vitro study [published online ahead of print, 2020 Jun 19]. J Esthet Restor Dent. 2020;10.1111/jerd.12611. doi:10.1111/jerd.12611
• Gül P, Akgül N. Farklı kompozit rezinlerin translüsensi ve maskeleme özelliklerinin karşılaştırılması. Dent Fac Atatürk Uni. 2013;21:30–6.
• Commission Internationale de L’Eclairage. CIE 15: Technical Report: Colorimetry 2004; 552.
• Pérez MM, Ghinea R, Ugarte-Alván LI, Pulgar R, Paravina RD. Color and translucency in silorane-based resin composite compared to universal and nanofilled composites. J Dent. 2010;38 Suppl 2:e110-e116.
• Johnston WM, Reisbick MH. Color and translucency changes during and after curing of esthetic restorative materials. Dent Mater. 1997;13:89-97.
• Lee YK, Lim BS, Rhee SH, Yang HC, Powers JM. Color and translucency of A2 shade resin composites after curing, polishing and thermocycling. Oper Dent. 2005;30:436-42.
• Güler E, Yücel A, Gönülol N, Yılmaz F, Ersöz E. Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. J Dent Fac Atatürk Uni. 2013;21:24–9.
• Harorlı OT, Barutcigil C. Color recovery effect of commercial mouth rinses on a discolored composite. J Esthet Restor Dent. 2014;26:256-63.
• Paravina RD, Ghinea R, Herrera LJ, et al. Color difference thresholds in dentistry. J Esthet Restor Dent. 2015;27 Suppl 1:S1-S9.
• Haas K, Azhar G, Wood DJ, Moharamzadeh K, van Noort R. The effects of different opacifiers on the translucency of experimental dental composite resins. Dent Mater. 2017;33:e310-6.
• Mutlu ŞN, Tuncdemir MT. Beyazlatıcı ağız gargarasının renklendirilmiş kompozit rezinin renk değişimine ve yüzey pürüzlülüğüne etkisi. Selcuk Dent J. 2020;7:435–9.
• Ghinea R, Pérez MM, Herrera LJ, Rivas MJ, Yebra A, Paravina RD. Color difference thresholds in dental ceramics. J Dent. 2010;38 Suppl 2:e57-64.
• Malekipour MR, Sharafi A, Kazemi S, Khazaei S, Shirani F. Comparison of color stability of a composite resin in different color media. Dent Res J (Isfahan). 2012;9:441-6.
• Zajkani E, Abdoh Tabrizi M, Ghasemi A, Torabzade H, Kharazifard M. Effect of staining solutions and repolishing on composite resin color change. JIDA. 2013;25:139–46.
• Poggio C, Vialba L, Berardengo A, et al. Color Stability of New Esthetic Restorative Materials: A Spectrophotometric Analysis. J Funct Biomater. 2017;8:26.
• Cangül S, Adıgüzel Ö, Ünal S, Tekin S, Sonkaya E, Erpaçal B. Investigation of the color stability of kept composite resins in different coffee types. Yeditepe Dent J. 2020;16:117–22.
• Ertaş E, Güler AU, Yücel AC, Köprülü H, Güler E. Color stability of resin composites after immersion in different drinks. Dent Mater J. 2006;25:371-6.
• Saraç D, Saraç YŞ, Külünk Ş, Kural Ç, Külünk T. Farklı inorganik dol- durucu içerikli kompozit rezinlerin renk sabitliği üzerinde polisaj yön- temlerinin ve yüzey verniği uygulamasının etkisi. GÜ Diş Hek Fak Derg. 2006;23:169-75.
• Tuncdemir AR, Güven ME. Effects of fibers on color and translucency changes of bulk-fill and anterior composites after accelerated aging. Biomed Res Int. 2018;2018:2908696.
• Turgut S, Bağış B, Bağış YH, Korkmaz FM, Tüzüner T, Baygın Ö. Restoratif materyallerin translüsensi özelliklerinin değerlendirilmesi. AÜ Diş Hek Fak Derg. 2011;38:18–20.
• Ryan EA, Tam LE, McComb D. Comparative translucency of esthetic composite resin restorative materials. J Can Dent Assoc. 2010;76:a84.
• Yu B, Lee YK. Influence of color parameters of resin composites on their translucency. Dent Mater. 2008;24:1236-42.
• Yu B, Lee YK. Translucency of varied brand and shade of resin composites. Am J Dent. 2008;21:229-32.
• Piccoli YB, Lima VP, Basso GR, Salgado VE, Lima GS, Moraes RR. Optical stability of high-translucency resin-based composites. Oper Dent. 2019;44:536–44.
• Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part I: core materials. J Prosthet Dent. 2002;88:4-9.
• Azzopardi N, Moharamzadeh K, Wood DJ, Martin N, van Noort R. Effect of resin matrix composition on the translucency of experimental dental composite resins. Dent Mater. 2009;25:1564-8.
• Pereira Sanchez N, Powers JM, Paravina RD. Instrumental and visual evaluation of the color adjustment potential of resin composites. J Esthet Restor Dent. 2019;31:465-70.
• Mikhail SS, Schricker SR, Azer SS, Brantley WA, Johnston WM. Optical characteristics of contemporary dental composite resin materials. J Dent. 2013;41:771-8.
• Lu H, Powers JM. Color stability of resin cements after accelerated aging. Am J Dent. 2004;17:354–8.
• Durand LB, Ruiz-López J, Perez BG, et al. Color, lightness, chroma, hue, and translucency adjustment potential of resin composites using CIEDE2000 color difference formula [published online ahead of print, 2020 Dec 7]. J Esthet Restor Dent. 2020;10.1111/jerd.12689. doi:10.1111/jerd.12689
• Morsy A, Gamal W, Riad M. Color matching of a single shade structurally colored universal resin composite with the surrounding hard dental tissues. EDJ. 2020;66:2721–7.
• Nikaido T, Kunzelmann KH, Chen H, et al. Evaluation of thermal cycling and mechanical loading on bond strength of a self-etching primer system to dentin. Dent Mater. 2002;18:269-75.
• Koyuturk AE, Kusgoz A, Ulker M, Yeşilyurt C. Effects of mechanical and thermal aging on microleakage of different fissure sealants. Dent Mater J. 2008;27:795–801.