Sintering Properties of Slip Casted Greek Red Mud Bodies

Yıl 2019, , 71 - 77, 15.12.2019

Nermin Demirkol , Vildan Samancı

https://doi.org/10.17100/nevbiltek.633834

Öz

Red mud is a solid waste residue of
the digestion of bauxite ores with caustic soda for alumina production. There
are several red mud sources in the world. The aim of this study was to identify
the sintering conditions and technological properties of slip casted Greek red
mud bodies. Chemical analysis of used greek red mud was determined by XRF. Slip
casted samples were prepared with 40 vol. % solid content and sintered at 900,
950 and 1000 °C for 2h, seperately. Sintering and technological properties were
determined by measuring density, firing shrinkage and water absorption.
Structural characterization was carried out with scanning electron microscopy
(SEM) and X-ray diffraction studies. The best density, water absorption, firing
shrinkage values were obtained with Greek red mud body sintered at 1000°C.
Artistic glaze was applied onto the Greek red mud bodies sintered at 1000°C.
Glaze-body interaction were determined.

Anahtar Kelimeler

sintering, red mud, ceramic, slip casting

Slip Dökümle Üretilmiş Yunan Kırmızı Çamur Bünyelerin Sinterleme Özellikleri

Öz

Kırmızı çamur, alümina üretimi için kostik sodalı boksit
cevherlerinin öğütülmesinde oluşan katı
atık artığıdır. Dünyada birkaç kırmızı çamur kaynağı vardır. Bu çalışmanın amacı, slip dökümle üretilmiş Yunan kırmızı çamur bünyelerin sinterleme koşullarını ve
teknolojik özelliklerini belirlemektir. Kullanılan
kırmızı çamurun
kimyasal analizi XRF ile belirlendi. Slip dökülmüş numuneler hacimce %40 katı içeriği
ile
hazırlandı ve ayrı ayrı 900, 950 ve 1000°C’de
2 saat süre ile sinterlendi. Sinterleme ve teknolojik özellikler yoğunluk, pişme çekilmesi ve su emme ölçümleri
ile tanımlandı. Yapısal karakterizasyon taramalı elektron mikroskobu (SEM) ve X-ışını çalışmaları ile gerçekleştirildi. En iyi yoğunluk, su emme, pişme çekilme değerleri 1000°C’de sinterlenen Yunan kırmızı çamur bünye ile elde edildi.
1000°C’de sinterlenen Yunan kırmızı çamur bünye üzerine artistik sır uygulandı. Sır-bünye etkileşimi tanımlandı.

Anahtar Kelimeler

sinterleme, kırmızı çamur, seramik, slip döküm

Kaynakça

• [1] Ziynan C., Yunlong Y.U.E., Ya Q.U., Sheng L.I.,Fengnion W.U. and Hongting L.I.U, Properties of Aluminosilicate Glasses Prepared by Red Mud with Various [Al2O3]/[CaO] Mass Ratios. Journal of Wuhan University of Technology-Mater.Sci.Ed.www.jwutms.net , 33(2), 363-367, 2018. [2]Sutar H., Mishra S.C., Sahoo S.K., Chakraverty A.P. and Maharana H.S., Progress of Red Mud Utilization: An Overview. American Chemical Science Journal 4(3), 255-279, 2014. [3]Demir I., Baspinar M.S. and Kahraman E., An Investigation Effect of Red Mud on the Properties of Fired Brick. Afyon Kocatepe University Journal of Science and Engineering, 14 QZ5785, 2014. [4]Reed J.S., Principles of Ceramic Processing. A Wiley-Interscience Publication, John&Wiley&Sons, Inc. pp.492, 1995. [5]Reijnders A., The Ceramic Process, European Ceramic Word Centre, A&C Black Publishers Limited., pp 46. 2005. [6]Demirkol N.,Technological and Physical Properties of Dry Pressed Red Mud Bodies Containing Chamotte. Arabian Journal of Geosciences, 12:278, 2019. [7] Kavanová M., Klouzková A. and Klouzek J., Characterization of the Interaction Between Glazes and Ceramic Bodies. Ceramics-Silikáty 61(3) 267-275, 2017.