Yıl 2008, Cilt: 3 Sayı: 4, 627 - 635, 01.05.2008

Ali Kaya Gür , Tülay Yıldız

Öz

In this study, high Cr at FeCrC powder was coated on the surface 0,3 C steel with PTA (plasma tungsten arc) method. The surfaces coated with PTA method were exanimate of surface wear SEM-EDS and XRD analysis.As a result of; in the coated layer was observer metal carburs and nitrurs. Coated layer were different loads and distancies of abrasive wear. Coating layer was observed increase of wear resistance and hardness to be proportions carburs and nitrurs.

Anahtar Kelimeler

PTA FeCrC N2 Cr(C N) Wear

N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ

Yıl 2008, Cilt: 3 Sayı: 4, 627 - 635, 01.05.2008

Ali Kaya Gür , Tülay Yıldız

Öz

Bu çalışmada; yüksek Cr'lu FeCrC tozu 0,3 C'lu çeliğin yüzeyine Plazma Transfer Ark (PTA) yöntemiyle kaplanmıştır. PTA yöntemiyle alaşımlandırılmış kaplama tabakaların aşınma yüzeylerinin SEM-EDS ve XRD analizleri incelenmiştir. Sonuç olarak; kaplama tabakasında metal karbürler ve nitrürlerin oluştuğu görülmüştür. Kaplama tabaksı farklı yük ve mesafelerde abrasiv aşınma testine tabi tutulmuştur. Kaplamanın karbür ve nitrür oranına bağlı olarak kaplama tabakasının sertliğinin ve aşınma direncinin arttığı görülmüştür.

Anahtar Kelimeler

PTA FeCrC N2 Cr(C N) AŞINMA

Toplam 0 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Elektrik Makinaları
Yazarlar

Ali Kaya Gür

Tülay Yıldız Bu kişi benim

Yayımlanma Tarihi 1 Mayıs 2008
Yayımlandığı Sayı Yıl 2008 Cilt: 3 Sayı: 4

Kaynak Göster

APA Gür, A. K., & Yıldız, T. (2008). N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ. Technological Applied Sciences, 3(4), 627-635. https://doi.org/10.12739/10.12739
AMA Gür AK, Yıldız T. N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ. NWSA. Mayıs 2008;3(4):627-635. doi:10.12739/10.12739
Chicago Gür, Ali Kaya, ve Tülay Yıldız. “N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ”. Technological Applied Sciences 3, sy. 4 (Mayıs 2008): 627-35. https://doi.org/10.12739/10.12739.
EndNote Gür AK, Yıldız T (01 Mayıs 2008) N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ. Technological Applied Sciences 3 4 627–635.
IEEE A. K. Gür ve T. Yıldız, “N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ”, NWSA, c. 3, sy. 4, ss. 627–635, 2008, doi: 10.12739/10.12739.
ISNAD Gür, Ali Kaya - Yıldız, Tülay. “N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ”. Technological Applied Sciences 3/4 (Mayıs 2008), 627-635. https://doi.org/10.12739/10.12739.
JAMA Gür AK, Yıldız T. N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ. NWSA. 2008;3:627–635.
MLA Gür, Ali Kaya ve Tülay Yıldız. “N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ”. Technological Applied Sciences, c. 3, sy. 4, 2008, ss. 627-35, doi:10.12739/10.12739.
Vancouver Gür AK, Yıldız T. N2 GAZI ORANININ KAPLAMA TABAKASININ AŞINMA DAVRANIŞINA ETKİSİ. NWSA. 2008;3(4):627-35.